SLAB PORTLAND-SLAG CEMENT CEM II/B-S 32,5 R

PORTLAND-SLAG CEMENT CEM II/B-S 32,5 R

COMPOSITION OF CEMENT

  • Portland clinker cement in an amount of 65-79%
  • granulated blast furnace slag in an amount of 21-35%
  • minor constituents in an amount of 0-5%
  • setting time regulator - calcium sulphate

PROPERTIES

  • density 3,03 kg/dm3
  • bulk density 1,41 t/m3
  • high strength in long periods of maturation
  • moderate early strength growth dynamics
  • extended binding times
  • moderate heat of hydration
  • low shrinkage
  • good workability
  • increased resistance to chemical attack
  • light colour

FIELD OF APPLICATION

  • freight concrete according to PN-EN 206-1
  • structures and monolithic or prefabricated elements
  • concrete foundation
  • concrete for hydraulic engineering constructions
  • concrete for underground structures (culverts, tunnels)
  • soil stabilization and substructures of roads
  • "bricklaying and plastering" mortars
  • "lean" concrete for the foundation of supporting structures

CEMENT SATISFIES THE REQUIREMENTS OF:

  • EN 197-1:2011 "Cement - Part 1: Composition, specifications and compliance criteria for common use cements" standard.
  • EN 197-2:2014 "Cement - Part 2: Conformity assessment" standard.

Requirements according to EN 197-1 UNIT REQUIRED VALUES
Compressive strength after: 2 days MPa ≥ 10,0
Compressive strength after: 28 days MPa ≥ 32,5 ≤ 52,5
Binding time: (start) min ≥ 75
Soundness mm ≤ 10
Sulphate content (as SO3) % ≤ 3,5
Chloride content % ≤ 0,10
Chrome content - Cr (VI) ppm ≤ 2,0